Consultancy services for failure investigation and testing for the three KNPC refineries: failure investigation of tubes from feed stripper heat exchanger at the Mina Al-AHmadi refinery

2010

KISR Report

Technical Report No. 18

المساهمون:  Raid, W.T.

الموضوعات:  Heat exchanger ,  Microscopy ,  Longitude ruptures, ductile-brittle transition temperature, mechanical properties ,  الخواص الميكانيكية; درجة حرارة الإنتقال من اللدن إلى القصف;التمزقات الطويلة

المشروعات:  Consultancy Services for Failure Investigations and Testing for the Three KNPC Refineries

رمز المشروع:  PF 013S

عرض الملف

Consultancy services for failure investigation and testing for the three KNPC refineries: Failure investigation of boiler tubes at the Mina Al-Ahmadi Refinery,

2009

KISR Report

Technical Report No. 12

المساهمون:  Riad, W. T.

الموضوعات:  Corrosion resistance ,  Heat--Transmission ,  External surface, long-term overheating, creep ,  السطح الخارجي; زيادة التسخين على المدى الطويل ; الزحف

المشروعات:  Consultancy Services for Failure Investigations and Testing for the Three KNPC Refineries

رمز المشروع:  PF 013S

عرض الملف

Failure analysis of internally coated elbow,

KISR Report

Technical Report

المساهمون:  Al-Hadaj, M.GH.

الموضوعات:  Petroleum ,  Protective coatings ,  Corrosion-fatigue, cracking, turbulent flow, erosion ,  تآكل; إجهاد;تصدع; تدفق مضطرب; نحت

المشروعات:  Consultancy Services for Failure Investigations and Testing for the Three KNPC Refineries

رمز المشروع:  PF 013S

عرض الملف

Consultancy Services for Failure Investigation and Testing for the Three KNPC Refineries Failure Inveatigation of Tubes From Waste Heat Boiler at the Mina Al-Ahmadi Refinery.

2009

KISR Report

Technical Report No.15

المساهمون:  Riad, W. T.

الموضوعات:  التدفق الحراري ; تشوه انابيب المرجل ; زيادة التسخين ,  heat flux ; boiler tube deformation ; overheating

المشروعات:  Consultancy Services for Failure Investigations and Testing for the Three KNPC Refineries

رمز المشروع:  PF 013S

عرض الملف

Evaluation of the high temperature hydrogen attack susceptibility of V-02-01A and E-02-01 at Shuaiba refinery

2007

KISR Report

Technical Report No.1

المساهمون:  Ravindranath, K.

الموضوعات:  Hydrogen attack. ,  C-0.5 Mo steel. ,  Remaining life. ,  Safety. ,  Reliability. ,  Refinery equipment. ,  In-situmetallography.

المشروعات:  Consultancy Services for Failure Investigations and Testing for the Three KNPC Refineries

رمز المشروع:  PF 013S

عرض الملف